PERCOBAAN PEMBUATAN FASA INTERMETALIK Nb3Sn DENGAN PROSES SINTERING LOGAM NIOBIUM (Nb) DAN TIMAH (Sn)

Article Sidebar

PDF
Published: Dec 5, 2011
DOI: https://doi.org/10.14203/metalurgi.v26i3.19
Keywords:
MRI, NMR, Maglev, Superkonduktor Cu-Nb-Sn, Nano dalam tabung, Superkonduktor temperatur rendah, Nb3Sn, Nano-powder-in-tube, Low temperature superconductor

Main Article Content

Florentinus Firdiyono
Pusat Penelitian Metalurgi – LIPI
Andika Widya Pramono
Pius Sebleku
Nurhayati Indah Ciptasari
Anton Suryantoro

Abstract

Determination of optimum conditions include milling time of Nb and Sn with HEM, ratio of Nb and Sn, heating time and heating temperature of mixed Nb and Sn. Characterization of Nb3Sn produced from the process was performed using DTA, XRD, SEM and EDS. The results of SEM and XRD analysis showed the minimum time needed for milling Nb and Sn are 3 hours, and the result of DTA analysis showed the intermetalic phase of Nb3Sn was occured at the temparetuir around 700 °C. The result of XRD analysis for mixed Nb and Sn showed that by the increasing of heating time will produced more intermetalic phase of Nb3Sn.

Article Details

How to Cite
Firdiyono, F., Pramono, A. W., Sebleku, P., Ciptasari, N. I., & Suryantoro, A. (2011). PERCOBAAN PEMBUATAN FASA INTERMETALIK Nb3Sn DENGAN PROSES SINTERING LOGAM NIOBIUM (Nb) DAN TIMAH (Sn). Jurnal Metalurgi, 26(3), 137–148. https://doi.org/10.14203/metalurgi.v26i3.19
Issue
Vol. 26 No. 3 (2011): Metalurgi
Section
Articles
Creative Commons License

This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

References

Brochure “Superconductivity: Present and future Applications” by Coalation for the Commercial Application of Superconductors (CCAS) and IEEE council on Superconductivity, 2008.

Smith, W.F., Principles of Materials Science and Engineering, 3 nd Edition, McGraw -Hill, 1996, p. 855.

Larbalesteir, D., Superconductors for superconducting magnets, Applied superconductivity Center, National High Magnetic Field Laboratory, Florida State University, May 20, 2010.

Lee, P. J. : “Superconductor: WIRES AND CABLES: MATERIALS AND PROCESSES”, The Applied Superconductivity Center, University of Wisconsin, Madison, USA.

Hopkins, S. C., Optimisation, Characterisation and Synthesis of Low Temperaturs Supercoductors by Current- Voltage Techniques, PhD Thesis, Sidney Sussex College, Department of Materials Science and Metalurgy, 2007.Fischer, C. M., Investigation of the Relationships Between Superconducting Properties and Nb 3 Sn Reaction Conditions in Powder-In -Tube Nb 3 Sn Conductors, Master of Science Thesis, University of Wisconsin -Madison, 2002.

Patankar, S. N and Froes, F. H. Formation of Nb 3 Sn Using Mecha nically Alloyed Nb -Sn Powder. Institute for Materials and Advanced Processes, University of Idaho, Moscow.