THE UTILIZATION OF PET WASTE AS RAW MATERIAL FOR PRODUCING MONOFILAMENT YARN : THE EFFECT OF WINDING SPEED ON THE PHYSICAL AND MECHANICAL PROPERTIES OF THE YARN
Keywords:
plastic waste, PET, Melt spinning, Monofilament yarnAbstract
Plastic waste production in Indonesia is quite high, reaching 15% to the total national waste production or 189-kilo tons/day with an average growth of 14.7% per year, the second biggest contributor after organic waste. This fact greatly affects human health and the environment since plastic is difficult to degrade, estimated to require 100 to 500 years for the plastic to decompose completely. Therefore, recycling becomes a popular solution to reduce waste or plastic waste by turning it into new products that have added value. Plastic materials, such as PET, have thermoplastic properties which become a special potential to use as recycled materials. The aim of this research was to study the ability of PET plastic waste as a raw material for making monofilament yarn by melt-spinning methods. PET plastic waste is melted at 250-260 °C, then is extruded using a prototype melt-spinning tool with a single spinneret hole which the diameter is 3 mm into a monofilament yarn using three variations of winding speed (a) 43.33 m/min, (b) 59.35 m/min and (c) 72.72 m/min The results showed that the yarn with the highest winding speed (variation C) produced yarn with the highest fineness, reaching (30.06± 4.82) denier, and the best tensile strength compared with the other, reaching (47.7±14,97) MPa with elongation of of (10± 9.65) %.
Downloads
References
H. P. Putra dan Y. Yuriandala, “Studi Pemanfaatan Sampah Plastik Menjadi Produk dan Jasa Kreatif,” J. Sains &Teknologi Lingkung., vol. 2, no. 1, hal. 21–31, 2010, doi: 10.20885/jstl.vol2.iss1.art3.
A. D. A. Jatmiko Wahyudi, Hermain Teguh Prayitno, “Pemanfaatan Limbah Plastik Sebagai Bahan Baku Pembuatan Bahan Bakar Alternatif,” J. Litbang, vol. XIV, no. 1, hal. 58–67, 2018.
M. Syamsiro dkk., “Fuel oil production from municipal plastic wastes in sequential pyrolysis and catalytic reforming reactors,” Energy Procedia, vol. 47, hal. 180–188, 2014, doi: 10.1016/j.egypro.2014.01.212.
N. Karuniastuti, “Bahaya Plastik terhadap Kesehatan dan Lingkungan,” Swara Patra Maj. Pusdiklat Migas, vol. 3, no. 1, hal. 6–14, 2013.
F. Rian, “PRA RANCANGAN PABRIK BENANG POY 165 / 96 SDC DENGAN KAPASITAS 8.000 TON / TAHUN,” Tugas Akhir, Univ. Islam Indones., 2018.
S. Chowdhury, A. T. Maniar, dan O. Suganya, “Polyethylene Terephthalate ( PET ) Waste as Building Solution,” Int. J. Chem. Environ. Biol. Sci., vol. 1, no. 2, hal. 2320–4087, 2013.
U. B. Surono, “Berbagai Metode Konversi Sampah Plastik,” J. Tek., vol. 3, no. 1, hal. 32–40, 2013.
S. Das dan S. Paney, “Pyrolysis and Catalytic Cracking of Municipal Plastic Waste for Recovery of Gasoline Range Hydrocarbons Pyrolysis and Catalytic Cracking of Municipal Plastic Waste for Recovery of Gasoline Range Hydrocarbons,”
Thesis Natl. Inst. Technol. Rourkela, hal. 10–55, 2007.
N. K. Madi, “Thermal and mechanical properties of injection molded recycled high density polyethylene blends with virgin isotactic polypropylene,” Mater. Des., vol. 46, hal. 435–441, 2013, doi: 10.1016/j.matdes.2012.10.004.
E. Devaux, Understanding the behaviour of synthetic polymer fibres during spinning. Woodhead Publishing Limited, 2014.
B. Hu, S. Serranti, N. Fraunholcz, F. Di Maio, dan G. Bonifazi, “Recycling-oriented characterization of polyolefin packaging waste,” Waste Manag., vol. 33, no. 3, hal. 574–584, 2013, doi: 10.1016/ j.wasman.2012.11.018.
Dulmalik, A. Chafidz, R. Fernandi, dan Ardianto, “Partially Oriented Yarn (POY) produced from semidull via melting spun using an extruder: Effect of die extruder temperature on elongation of the POY,” J. Phys. Conf. Ser., vol. 1295, no. 1, 2019, doi: 10.1088/1742-6596/1295/1/012010.
E. M. Aizenshtein, “BOTTLE WASTES “ TO TEXTILE YARNS,” vol. 47, no. 5, hal. 3–7, 2020, doi: 10.1007/s10692-016 9691-8.
Noerati, A. S. Soekoco, M. Komalasari, Kurniawan, dan A. Hananto, “Pembuatan Serat Tekstil Bukan Sandang dari Limbah kantong plastik polietilen,” Semin. Utomo Pemanfaat. Sumber Daya Alam untuk Meningkat. Daya Saing Ind. Proses Nas. . ITENAS, hal. kimia 1-3, 2016.
Q. Xu, H. Yi, X. Gao, J. Shi, dan D. Yao, “Recycling of Polyethylene Bags into High-Strength Yarns Without Using Melt Processing,” Polym. Eng. Sci., vol. 60, no. 2, hal. 281–287, 2020, doi: 10.1002/ pen.25281.
F. A. Reifler, R. Hufenus, M. Krehel, E. Zgraggen, R. M. Rossi, dan L. J. Scherer, “Polymer optical fibers for textile applications - Bicomponent melt spinning from cyclic olefin polymer and structural characteristics revealed by wide angle X-ray diffraction,” Polymer (Guildf)., vol. 55, no. 22, hal. 5695–5707, 2014, doi: 10.1016/ j.polymer.2014.08.071.
S. M. Ghoreishian dkk., “Optimization of meltspinning parameters of poly(ethylene terephthalate) partially oriented multi-filament yarn in an industrial scale: Central composite design approach,” Fibers Polym., vol. 18, no. 7, hal. 1280– 1287, 2017, doi: 10.1007/s12221-017-1119-4.
M. Norouzi, Y. Zare, dan P. Kiany, “Nanoparticles as effective flame retardants for natural and synthetic textile polymers: Application, mechanism, and optimization,” Polym. Rev., vol. 55, no. 3, hal. 531–560, 2015, doi: 10.1080/15583724.2014.980427.
M. Norouzi, L. M.-A. J. of Chemistry, dan undefined 2010, “Photocatalytic Effects of Nanoparticles of TiO^ sub 2^ in Order to Design Self-Cleaning Textiles,” Asian J. Chem.
M. Norouzi, B. Nazari, dan D. W. Miller, “Injectable hydrogel-based drug delivery systems for local cancer therapy,” Drug Discov. Today, vol. 21, no. 11, hal. 1835–1849, 2016, doi: 10.1016/ j.drudis.2016.07.006.
O. Babaarslan dan S. Ö. Hacioçullari, “Effect of fibre cross-sectional shape on the properties of POY continuous filaments yarns,” Fibers Polym., vol. 14, no. 1, hal. 146–151, 2013, doi: 10.1007/ s12221-013-0146-z.
A. Ferreira, F. Ferreira, dan M. C. Paiva, “Textile Sensor Applications with Composite Monofilaments of Polymer / Carbon Nanotubes,” Adv. Sci. Technol., vol. 80, hal. 65–70, 2012, doi: 10.4028/www.scientific.net/ast.80.65.
J. Hagewood, Technologies for the manufacture of synthetic polymer fibers. Woodhead Publishing Limited, 2014.
A. S. Soekoco, D. Mustafa, Rosmawat, dan Jane, “Recycled fiber from straw waste: Effect of takeup speed and spinneret diameter to linear density and tenacity,” MATEC Web Conf., vol. 154, hal. 2–5, 2018, doi: 10.1051/matecconf/201815401119.
A. Rawal dan S. Mukhopadhyay, Melt spinning of synthetic polymeric filaments, no. 1976. Woodhead Publishing Limited, 2014.
K. Hari, P, “Types and properties of fibres and yarns used in weaving 1,” in Woven Textile, Woodhead Publishing Limited, 2012, hal. 3–34.
A. P. Dos Santos Pereira, M. H. P. Da Silva, É. P. Lima, A. Dos Santos Paula, dan F. J. Tommasini, “Processing and characterization of PET composites reinforced with geopolymer concrete waste,” Mater. Res., vol. 20, hal. 411–420, 2017, doi: 10.1590/1980-5373-MR-2017-0734.
S. . Zhurkov, I. . Novak, B. Y. Levin, A. . Savitskii, dan V. . Vettegren, “Relation Between Polymer Strength And Molf~Ular Orientation,” no. 7, hal. 1203–1207, 1965.
A. J. Uddin, Y. Ohkoshi, Y. Gotoh, M. Nagura, R. Endo, dan T. Hara, “Effects of take-up speed of melt spinning on the structure and mechanical properties of maximally laser drawn PA9-T fibers,” Int. Polym. Process., vol. 21, no. 3, hal. 263–271, 2006, doi: 10.3139/217.0090.
Downloads
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.