GROWTH OF CARBON NANOTUBE FROM NANOSTRUCTURED COMPOSITE OF Fe-C USING ION IMPLANTATION TECHNIQUE
Keywords:
Carbon Nanotube, Integrated Sensor System, Composite of Fe-C, Ion ImplantationAbstract
GROWTH OF CARBON NANOTUBE FROM NANOSTRUCTURED COMPOSITE OF Fe-C USING ION IMPLANTATION TECHNIQUE. Growth of carbon nanotube (CNT) from nanostructured composite of Fe-C has been carried out using ion implantation technique. The CNT developed here is expected to be used as an Integrated Sensor System, because CNT offer promises for future nano-electronic sensor applications, and reliably controlling CNT growth has been a big challenge. Nanostructured composite of Fe-C was prepared by milling for 50 hours. The size of Fe-C powder was determined from Scanning Electron Microscope (SEM) image. Milled powder then was compressed to get pellet form of Fe-C, and used as a target in fabricating thin film of Fe-C on Si(100) substrate using sputtering technique. Further, the ion implantation was done against the Fe-C thin film. The ion source using Argon gas, in order to make growth of CNT until the densitiy dose of 5 x 1015 ions/cm2 . The phase of formed CNT was identified by X-Ray Diffractometer (XRD), the morphology of surface was observed by SEM. From this research, it has been showed that the milled composite of Fe-C has a powder size until nano order size. From XRD data, it is identified that only Fe and C peaks were confirmed. On the other hand, the observation on the surface of Fe-C thin film showed the growth of CNT
Downloads
References
. J.H.J. SCOTT and S.A. MAJETICH, Phys. Rev. B,
(1995) 12564
. P. TARTAJ, M.P. MORALES, S. VEINTEMILLASVERDAGUER,T.GONZALEZ-CARRENOandC.J.
SERNA, J. Phys. D: Appl. Phys., 36 (2003) R182
. X.Q. ZHAO, Y. LIANG, Z.Q. HU and B.X. LIU,
J. Appl. Phys., 80 (1996) 5857
. C.A. GRIME, J.L. HORN, G.G. BUSH, J.L.ALLEN
and P.C. EKLUND, IEEE Trans. Magn., 33 (1997)
. C.A.GRIMES,D.QIAN,E.C.DICKEY,J.L.ALLEN
and P.C. EKLUND, J Appl. Phy., 87 (2000) 5642
. F.S. DENES, S. MANOLACHE, Y.C. MA, V.
SHAMAMIAN, B. RAVEL and S. PROKES,
J. Appl. Phy., 94 (2003) 3498
. J.L. WILSON, P. PODDAR, N.A. FREY, H.
SRIHANT, K. MOHOMED, J.P. HARMON, S.
KOTHA and J. WACHSMUTH, J. Appl. Phys., 95
(2004)1439
. H.M. KIM, K. KIM, C.Y. LEE, J. JOO, S.J. CHO,
H.S.YOON, D.A. PEJAKOVIC, J.W.YOO and A.J.
EPSTEIN, Appl. Phys. Lett., 84 (2004) 589
. R.MARTEL,T.SCHMIDT, H.R.SHEA,T. HERTEL
and P.AVOURIS, Appl. Phys. Lett., 73 (1998) 2447
. S.J. TRANS, A.R.M. VERSHUEREN and C.
DEKKER,Nature, 393 (1998) 49
. A. JAVEY, J. GUO, Q. WANG, M. LUNDSTROM
and H. DAI, Nature, 424 (2003) 654
. H.W.C. POSTMA, T. TEEPEN, Z. YAO, M.
GRIFONI and C. DEKKER, Science, 293 (2001) 76
. Z. YAO, H.W.C. POSTMA, L. BALENTS and C.
DEKKER,Nature, 402 (1999) 273
. R.H. BAUGHMAN, A.A. ZAKHIDOV and W.A.
DE HEER, Science, 297 (2002) 787
. P.AVOURIS, J.APPENZELLER, R. MARTEL, and
SHALOM J. WIND, Carbon Nanotube Electronics,
Proc. of the IEEE, 91 (11) (2003) 1772-1783
. M.LOYA,J.E.PARK,L.H.CHEN,K.S.BRAMMER,
P.R. BANDARU and S. JIN, Nano: Brief Report
and Reviews, 3 (2008) 449-454
. SALIM MUSTOFA and YUNASFI, Indonesian
Journal of Materials Science, 10 (3) (2009)
-291
. J.R. HARRIS, Mathematical Modelling of
Mechanical Alloying, Thesis Submitted to The
University of Nottingham for the Degree of Doctor
of Phylosophy, (2006)
Downloads
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.