OPTIMIZATION OF MECHANICAL STRENGTH AND MICROSTRUCTURE ON AUSTEMPERING ZINC HEAT TREATMENT IN LATERITIC NICKEL STEELS
DOI:
https://doi.org/10.17146/jsmi.2019.20.4.4660Keywords:
Baja laterit, Heat treatment Austempering, Ketahanan impak, StrukturmikroAbstract
The development of lateritic steel is currently being discussed by various research institutions. It is not separated from the potential of laterite-based steel into national steel. This research using austempering heat treatment process with holding time variation for 30, 60, and 90 minutes with Zn (Zinc) element from melting ingot with 90% purity for cooling media. The characterization of laterite steel is done by hardness testing, impact resistance, microstructure, scanning electron microscopy, and energy dispersive spectroscopy. The results showed that the impact resistance value decreased 8.46%, which was initially 209 J to 191.3 J. Besides, the hardness value increased 36, 58% of which was originally 164 HV to 224 HV. Judging from its physical properties, the microstructure formed bainite ferrite perlite at holding time 90 minutes while the fracture is included into the ductile fracture because there are dimple holes showed dark and opaque
Downloads
References
. Saefudin, T. B. Romijarso, and D. P. Malau,
“Pembuatan Struktur Dual Phase Baja Aisi 3120H
Dari Besi Laterit,” no. November, pp. 1–5, 2016.
. P. Prasetiyo, “Tidak sederhana mewujudkan
industri pengolahan nikel laterit kadar rendah di
Indonesia sehubungan dengan Undang-Undang
Minerba 2009,” J. Teknol. Miner. dan Batubara,
vol. 12, no. 3, pp. 195–207, 2017.
. M. Yunan Hasbi, D. Panghihutan Malau, and B.
Adjiantoro, “Pengaruh Variasi Reduksi Terhadap
Kekerasan dan Struktur Mikro Baja Laterit Melalui
Pengerolan Panas,” Pros. Semin. Nas. Sains dan
Teknol., no. November, pp. 1–8, 2016.
. A. D. Clark, D. O. Northwood, R. J. Bowers, X. Sun,
P. Bauerle, and C. G. Llc, “Comparison of
Austempering and Quench-and-Tempering
Processes for Carburized Automotive Steels,” SAE
Int. J. Mater. Manuf., vol. 6, no. 2, pp. 146–153,
. N. Niazi, S. Nisar, and A. Shah, “Austempering Heat
Treatment of AISI 4340 Steel and Comparative
Analysis of Various Physical Properties at Different
Parameters,” Int. J. Multidiscip. Sci. Eng., vol. 5,
no. 10, pp. 6–11, 2014.
. X. Han et al., “Austenite-Bainite Transformation
Kinetics in Austempered AISI 5160 Steel,” Eur. Sci.
J., vol. 14, no. 12, pp. 1–14, 2018.
. Franco Dwiky Praguna, M. S. Anwar, E. Mabruri,
and Sunardi, “KETAHANAN IMPAK ,
KEKERASAN DAN STRUKTURMIKRO
DENGAN VARIASI SUHU PERLAKUAN PANAS
Hasil Uji Kekerasan dengan Variasi Suhu Austenisasi dan Suhu Tempering,” J. Sains Mater.
Indones., vol. 19, no. 3, pp. 125–130, 2018.
. G. E. Totten, “Steel Heat Treatment,” Steel Heat
Treat. Handb., 2006.
. S. Herbirowo, B. Adjiantoro, and F. Citrawati,
“Karakteristik Sifat Mekanik dan Strukturmikro Baja
Laterit Paduan Ni-Cr-Mn Hasil Tempa Panas
Dengan Variasi Beban Tempa,” Maj. Metal., vol. 1,
pp. 35–42, 2018.
. B. V. de Souza, T. M. Ribeiro, A. Francois, and C. A.
dos Santos, “Austempering heat treatments of
ductile iron using molten metal baths,” Mater.
Manuf. Process., vol. 33, no. 15, pp. 1–7, 2018.
. S. Herbirowo, L. Hakim, and B. Adjiantoro,
“Microstructure and mechanical characteristics of
hot forged lateritic steels,” MATEC web Conf., vol.
, no. 05007, pp. 1–6, 2018.
Downloads
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.