PENGARUH TEKNIK BEKU LELEH DAN DOSIS IRADIASI GAMMA PADA PELEPASAN RESORSINOL DARI MATRIKS HIDROGEL POLIVINIL ALKOHOL

Abstract

PENGARUH TEKNIK BEKU LELEH DAN DOSIS IRADIASI GAMMA PADA PELEPASAN RESORSINOL DARI MATRIKS HIDROGEL POLIVINILALKOHOL. Hidrogel adalah polimer dengan struktur tiga dimensi memungkinkan zat bioaktif terimobilisasi di dalam matriksnya dan dimanfaatkan sebagai sistem obat lepas terkendali. Telah dilakukan imobilisasi resorsinol dalam hidrogel Poli Vinil Alkohol (PVA) dengan teknik kombinasi beku leleh (1 siklus hingga 3 siklus) dan iradiasi gamma (10 kGy hingga 30 kGy). Hidrogel dikarakterisasi dengan spektrofotometer Fourier Transform-InfraRed (FT-IR). Fraksi gel dan daya serap air ditentukan secara gravimetri, dan pelepasan resorsinol diukur dengan spektrofotomer UltravioletVisible (UV-Vis). Hasil evaluasi menunjukkan bahwa dengan meningkatnya siklus beku leleh hingga 3 siklus dan dosis iradiasi 30 kGy meningkatkan fraksi gel 95%. Sebaliknya kemampuan daya serap air menurun dari 600% ke 200%, pola penurunan ini (kondisi yang sama) sesuai dengan penurunan kemampuan release resorsinol dari 88% ke 59%. Proses sistem beku leleh dan iradiasi selayaknya dapat dipertimbangkan sebagai salah satu sistem imobilisasi obat terkendali.

ABSTRACT

EFFECT OF FREEZE THAWING TECHNIQUE AND GAMMA IRRADIATION TO RESORCINOL RELEASE FROM MATRIX OF POLYVINYL ALCOHOL. Hydrogels are polymers with three-dimensional structure that useful to immobilize drugs as sustained release system. Immobilization of resorcinol in the polyvinyl alcohol hydrogel (PVA) is prepared by combination of freeze thawing (1-3 cycles) and gamma irradiation (10-30 Gy). The chemical structure of hydrogels was characterized by Fourier Transform- Infra Red (FT-IR) spectrophotometer. Gel fraction and water absorption were measured by gravimetry. The release of resorcinol was determined by Ultraviolet-Visible (UV-Vis) spectrophotometer. The results of evaluation showed that by increasing the number freeze-thawing up to 3 cycles and irradiation dose to 30 kGy, the gel fraction can reach up 95%. In contrast, the water absorption of hydrogels decreases from 600% to 200%, and the decreasing release profile of water absorption of hydrogels (at the same condition) was similar with the release profile of resorcinol from 88% to 59%. The combination of
freeze-thawing and gamma irradiation can be considered as one of the immobilization techniques for sustained drug release.