IMPROVING ANATASE TO RUTILE TRANSITION TEMPERATURE BY MILLING

Authors

  • Suminar Pratapa Department of Physics, Faculty of Mathematics and Natural Sciences - ITS Kampus ITS Keputih, Sukolilo, Surabaya 60111.
  • Triwikantoro Department of Physics, Faculty of Mathematics and Natural Sciences - ITS Kampus ITS Keputih, Sukolilo, Surabaya 60111.
  • Hariyati Purwaningsih Department of Materials Engineering, Faculty of Industrial Engineering - ITS Kampus ITS Keputih, Sukolilo, Surabaya 60111.

DOI:

https://doi.org/10.17146/jsmi.2006.7.3.4833

Keywords:

Anatase to rutile transition, milling, x-ray diffraction

Abstract

IMPROVING ANATASE TO RUTILE TRANSITION TEMPERATURE BY MILLING.
An intensive investigation using X-ray diffractometry has been conducted to study the optimum mechanical
and thermal conditions for the transition of anatase-to-rutile from a titanium dioxide (TiO2
) powder. Milling
was applied by employing a conventional ball milling instrument and a quasi-high-energy pulveriser and
varying the milling period. Heat treatment was performed by calcination at 850, 900, 950, 975, 1000, 1050 and
1100°C for 1 hour, being the predicted optimum temperature to obtain fully rutile powder was 975°C. Each
powder was milled and then calcined prior to the X-ray diffraction investigation. X-ray diffraction data were
analysed using (1) standard identification and peak characterisation, (2) the Rietveld method to give the weight
fractions, lattice constants and crystallite size and strain estimates, and (3) Mozaix, an own-developed software
to provide strain, crystallite size and size distribution of phases. Results showed that milling speed and milling
up to 24 hours does not significantly change the phases’ composition, but enhances the transition temperature.
Conventional milling gives better results than pulverising. Conventional milling at 100 rpm for 3 hours reduces
the transition temperature from 1100°C to 1000°C. Longer milling, however, does not improve the transition
temperature. The optimum process is discussed and SEM micrographs are used to support the argument.

Downloads

Download data is not yet available.

References

. HOWARD, C. J., SABINE, T. M. and DICKSON, F.

, Structural and Thermal Parameters for Rutile and

Anatase, Acta Crystallographica B (39), (1983) 462-468

. SABINE, T. M. and HOWARD, C. J. , Determination of the Oxygen x Parameter in Rutile by Neutron Diffraction Method, Acta Crystallographica B (38) (1982)701-702

. PARK, S.-E. E. and HACKENBERGER, W , HighPerformance Single Crystal Piezoelectrics:

Applications and issues, Current Opinion in Solid

State and Materials Science, 6 (2002) 11-18

. SUASMORO, S., PRATAPA, S., HARTANTO, D.,

SETYOKO, D. and DANI, U. M. ,The

Characterisation of Mixed titanate Ba1-xSrxTiO3

Phase Formation from Oxalate Coprecipitated

Precursor, Journal of European Ceramic Society,

(3) (2000) 309-314.

. PRATAPA, S. and LOW, I. M. InfiltrationProcessed Functionally-Graded Aluminium Titanate/Zirconia-Alumina Composite: II, Mechanical Properties, J. Mater. Sci., 33 (1998)

-3053

. PRATAPA, S., HARTANTO, D. and APRILYANTI,

E, Liquid Infiltration Technique for the Synthesis

of Rutile-Alumina Functionally-Graded Material,

IPTEK (ITS Periodical), 12 (1) (2001) 21-29

. LEYLAND,N.S.;EVANS,J.R.G.and HARRISON,

D. J. , Lithographic Printing of Ceramics, Journal

of European Ceramic Society, 22 (2002) 1-13

. NAVROTSKY,A. and KLEPPA, O. J. , Enthalpy of

the Anatase-Rutile Transformation, J. Am. Ceram.

Soc., 50 (11) (1967) 626

. KOSTIC, E. M., KISS, S. J., BOSKOVIC, S. B. and

ZEC, S. P. , Mechanically Activated Transition of

Anatase to Rutile, The American Ceramic Society

Bulletin, 76 (6) (1997) 60-64

. NAN, C. W. and CLARKE, D. R., Effects of

Variation in Grain size and Grain Boundary Barrier

Heights on the Current-Voltage Characteristics of

ZnO Varistors, J. Am. Ceram. Soc., 79 (12) (1996)

-3192

. LANGFORD, J. I., LOUËR, D. and SCARDI, P. ,

Effect of a Crystallite Size Distribution on X-ray

Diffraction Line Profiles and Whole-PowderPattern Fitting, J. Appl. Cryst., 33 (2000) 964-974

. POPA, N. C. and BALZAR, D. , An Analytical

Approximation for a Size-Broadened Profile Given

by the lognormal and gamma distributions, J. Appl. Cryst., 35, (2002) 338-346.

. PRATAPA, S., Diffraction-Based Modelling of

Microstructural Size and Strain Effects in Sintered

Ceramics, PhD Thesis, Curtin University of

Technology, Perth, (2003)

. SPURS, R. A. and MYERS, H. , Quantitative

analysis of anatase-rutile mixture with x-ray

diffractometer, Anal. Chem. Res., 29 (1957) 760-762

. PAN, X. and MA, X. , Study on the MillingInduced Transformation in TiO2 Powder with Different Grain sizes, Mater. Lett., 8 (2004) 513-515

. FARREL, K. A. , Synthesis Effects on Grain Size

and Phase Content in the Anatase-Rutile TiO2

System, M.Sc. thesis, Worcester Polytechnic

Institute, (2001)

. ARROYO, R., CÓRDOBA, G., PADILLA, J. and

LARA, V. H. , Influence of Manganese ions on the

Anatase-Rutile Phase Transition of TiO2 Prepared

by the Sol-Gel Process, Mater. Lett., 54 (2002) 397-402

. HUNTER, B. A. , Rietica, In Newsletter of

International Union of Crystallography,

Commission on Powder Diffraction, Sydney, 20,

(1998)21

Downloads

Published

30-06-2006

How to Cite