MAGNETIC NANOSTRUCTURES : FABRICATION AND APPLICATIONS FROM MEMORY DEVICES TO BIOSENSOR
DOI:
https://doi.org/10.17146/jsmi.2014.15.3.4345Keywords:
Magnetic Nanostructures, Memory, Biosensor, Magnetite, Nanodots, Surface Plasmon ResonanceAbstract
MAGNETIC NANOSTRUCTURES : FABRICATION AND APPLICATIONS FROM MEMORY DEVICES TO BIOSENSOR. For magnetic storage application, we successfully fabricated nanodots and nanopattern using electron-beam lithography (EBL) technique followed by ion irradiation. Perpendicularly magnetized squared-bits with the sizes of 100 to 500 nmwere clearly observed using magnetic forcemicroscopy (MFM) images. MFM images showed that the most of the patterned squared-bits with size of 100 nm have either uniformly bright or dark magnetic contrasts. Magnetization curves of patterned films were strongly influenced by the bit size and spacing between bits and indicated the existence of exchange coupling between the bits via irradiated spacing. On the other hand, for biosensor application, we recently develop Surface Plasmon Resonance (SPR)-based biosensor for biomolecules detection device.Magnetic nanoparticles such as magnetite (Fe3O4) and CoFe2O4 were purposed as candidate for active materials to increase accumulation of target biomolecules on sensing surface of SPR-based biosensor. Fe3O4 and CoFe2O4 nanoparticles with different sizes of 8 to 17 nm have been successfully synthesized chemically by co-precipitation method. The surface of nanoparticles had been modified using polyethylene glycol (PEG)-4000 to increase the crystallinity, decrease agglomeration and control the shape to more spherical. However, modification using PEG-4000 decreased the saturation magnetization which is due to the existence of α-FeO(OH) and γ-FeO(OH) phases from bonds at interface of CoFe2O4.
Downloads
References
. P. R. Krauss, and S. Y. Chou. “Fabrication of Planar
Quantum Magnetic Disk Structure Using Electron
Beam Lithography, Reactive Ion Etching, and
Chemical Mechanical Polishing”. Journal of
Vacuum Science & Technology B, vol. 13 (6), pp.
-2852, Nov/Dec. 1995.
. L Kong, L Zhuang, and SY Chou. “Writing and
Reading 7.5 Gbits/in2 Longitudinal Quantized
Magnetic Disk Using Magnetic Force Microscope
Tips”. IEEE Transaction Magnetic. vol. 33(5), pp.
-3021, Sep. 1997.
. A. Fernandez, P.J. Bedrossian, S.L. Baker, S.P.
Vernon, and D.R. Kania. “Magnetic Force
Microscopy of Single-Domain Cobalt Dots
Patterned Using Interface Lithography”. IEEE
Transaction Magnetic. vol. 32 (5), pp. 4472-4474,
Sep. 1996.
. C. Chappert, H. Bernas, J. Ferre´ , V. Kottler, J.-P.
Jamet,Y. Chen, E. Cambril, T. Devolder, F.Rousseaux,V. Mathet, and H. Launois. “Planar
Patterned Magnetic Media Obtained by Ion
Irradiation”. Science, vol. 280, pp. 1919-1922, Jun.
. J. Ferré, C. Chapert, H. Bernas, J.P. Jamet, P. Meyer,
O. Kaitasov, S. Lemerle, V. Mathet, F. Rousseaux,
and H. Launios, “Irradiation Induced Effects on
Magnetic Properties of Pt/Co/Pt Ultrathin Films”.
Journal of Magnetism and Magnetic Materials,
vol. 198-199, pp. 191-193, Jun. 1999.
. A.H. Lu, E.L. Salabas, and F. Schüth, “Magnetic
Nanoparticles: Synthesis, Protection,
Functionalization and Application”, Angewandte
Chemie International Edition, vol. 46(8), pp. 1222-
, Feb. 2007.
. Y .F. Shen, J. Tang, Z.H. Nie, Y.D. Wang, Y. Ren,
and L. Zuo. “Tailoring Size and Structural
Distortion of Fe 3O4 Nanoparticles for The
Purification of Contaminated Water.” Bioresource
Technology, vol. 100, pp. 4139-4146, September.
. K.K. Senapati, C. Borgohain, and P. Phukan.
“Synthesis of Highly Stable CoFe2O4 Nanoparticles
and Their Use as Magnetically Separable Catalyst
for Knoevenagel Reaction in Aqueous Medium.”
Journal of Molecular Catalysis A: Chemical,
(1), pp. 24-41,April. 2011.
. G. F. Goya, T. S. Berquó, F. C. Fonseca, and M. P.
Morales, “Static and dynamic magnetic properties
of spherical magnetite nanoparticles”, Journal of
Applied Physics., vol. 94(5), pp. 3520-3528, 2003.
. T. Hyeon, “Chemical synthesis of magnetic
nanoparticles”, Chem. Commun., vol. 8, pp. 927-
2003.
. V.L. Del Castillo, “Synthesis and Characterization
of Cobalt-Substituted Ferrite Nanoparticles Using
Reverse Micelles”, Thesis, University of Puerto
Rico, Mayagüez Campus, 2005.
. Y. Ahn, E. J. Choi, and E. H. Kim.
“Superparamagnetic Relaxation in Cobalt Ferrite
Nanoparticles Synthesized from Hydroxide
Carbonate Precursors”, Rev. Adv. Mater. Sci. 5, pp.
,2003.
. E. Suharyadi, T. Kato, S. Tsunashima, and S. Iwata.
“”Magnetic Properties of Patterned Co/Pd
Nanostructures by E-Beam Lithography and Ga
Ion Irradiation” IEEE Transactions on Magnetics,
vol. 42, no. 10, pp. 2972, Oct. 2006.
. E. Suharyadi, S. Natsume, T. Kato, S. Tsunashima,
and S. Iwata. “Microstructures and Magnetic
Properties of the FIB Irradiated Co/Pd Multilayer
Films”, IEEE Transactions on Magnetics, vol. 41,
no. 10, pp. 3595, Oct. 2005.
. E. Suharyadi, D. Oshima, T. Kato, and S. Iwata.
“Switching Field Distribution of Planar Patterned
CrPt3Nanodots Fabricated by Ion Irradiation”,
Journal of Applied Physics, 109, pp. pp. 07B771-
B773.2011.
. L.S. Birks, et.al., “Particle Size Determination from
X Ray Line Broadening”, J. Appl. Phys., vol.17,
pp. 687. 1946.
. E. Suharyadi, E. A. Setiadi, N. Shabrina , T. Kato,
and S. Iwata. “Magnetic Properties and
Microstructures of Polyethylene Glycol (PEG)-
Coated Cobalt Ferrite (CoFe2O4
) Nanoparticles
Synthesized by Coprecipitation Method”.
Advanced Materials Research, vol. 896, pp 126-
2014.
. Y.I. Kim, D. Kim, and C. S. Lee. “Synthesis and
Characterization of CoFe 2O4 Magnetic
Nanoparticles Prepared by Temperature-controlled
Coprecipitation Method”, Physica B, vol. 337, pp.
-51.2003.
. E. Suharyadi, S. Natsume, T. Kato, S. Tsunashima,
and S. Iwata. “Modification of the Microstructure
and Magnetic Properties of Ga-Ion Irradiated Co/
Pd Multilayer Film for Future Planar Media”, Trans.
of the Magn. Soc. Jap., vol. 5 no. 3, pp. 125. 2005
Downloads
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.