PREPARATION OF LEAD MAGNESIUM NIOBATE-LEAD ZIRCONATE TITANATE FILMS AND THEIR CRYSTALLIZATION BEHAVIORS
DOI:
https://doi.org/10.17146/jsmi.2002.3.3.5058Keywords:
PMN-PT-PZ films, sol-gel, crystallization, perovskiteAbstract
PREPARATION OF LEAD MAGNESIUM NIOBATE-LEAD ZIRCONATE TITANATE FILMS AND THEIR CRYSTALLIZATION BEHAVIORS. The thin films with composition near morpotropic phase boundary (MPB) of the system xPb(Mg1/3, Nb2/3)O3-yPbTiO3-zPbZrO3 (x = 0 – 0.35, y = 0.47 and z = 0.53), were prepared by sol-gel method. The starting materials were consisted of Pb(iso-OC3H7)2, Zr(n-OC4H9)4, Ti(iso-OC3H7)4, Mg(CH3COO)2 4H2O and Nb(OC2H5)5. The 1-propanol was used as solvent. The concentration of PMN-PT-PZ in coating solution was 0.7 M, and the pH of the solution was 4.5. The thin films were prepared by dipcoating and spincoating. The crystallization behaviors of the PMN-PT-PZ thin films showed that the formation of perovskite phase at low temperature becomes difficult with increasing the content of PMN. The amounts of pyrochlore and perovskite phase in PMN-PT-PZ films depended on the heating temperatures, and PMN contents. Single-phase perovskite was found for the coated films containing 0 and 12.5 mol% after calcinating at 600 oC, 21 mol% after calcinating at 700oC, and 30 mol% after calcinating at 750oC. Single-phase perovskite of coated films will never be found when the content of PMN was 35 mol%.
Downloads
References
[1]. AZAROFF, L.V., Introduction to Solids McGrawHill, NewYork, (1960)
[2]. JONA, F., and SHIRANE, G., Ferroelectric Crystals Macmillan, NewYork, (1962)
[3]. N. DE MATHAN, E. HUSSON, P. GAUCHER and A. MORELL, Mat. Res. Bull. 25, (1990) 427
[4]. CHANDLER, C.D., ROGER, C., and HAMPDENSMITH M., J. Chem. Rev. 93, (1993) 1205
[5]. K. OKUWADA, M. IMAI and K. KAKUNO, Jpn. J. Applied Physics, 28 (7) ,(1989) 1271
[6]. S.K. DEY, K.D. BUBB, and D.A. PAYNE, “ThinFilm Ferroelectrics of PZT by Sol-Gel Processing,” pp. 80 in IEEE Transactions on Ultrasonics, Ferroelectrics and Frequency Control, 35 (1), January (1988).
[7]. LORRAINE FALTER FRANCIS and D.A. PAYNE, MAT. Res. Soc. Symp. Proc., 200, (Material Reseach Society), 173 (1990)
[8]. J. BERNARD, R. WILLIAM, Jr. COOK and J. HANDS, Piezoelectric Ceramics, 124 (1971)
[9]. S.D. BERNSTEIN, Y. KISLE, J. M. WAHL, S.E. BERNACKI, and S.R. COLLINS, “Effects of Stoichiometry on PZT Thin Film Capacitor Properties”, pp. 373 in Ferroelectric Thin Films II,Proceedings of the Materials Research Society Symposium (Boston, MA, December, 1991). Edited by A. I. Kingon, E.R. Myers, and B. Tuttle. Materials Reasearch Society, Westerville, OH, (1992).
[10]. LORRAINE FALTER FRANCIS and D.A. PAYNE, J.Am. Ceram. Soc. 74 (12), (1991) 300
Downloads
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.