Study of the Effect of Ultraviolet Exposure Duration on Polypropylene Properties
DOI:
https://doi.org/10.55981/jsmi.2025.8959Keywords:
degradation, exposure, plastics, polypropylene, ultravioletAbstract
Prolonged exposure to ultraviolet (UV) radiation significantly alters the chemical, thermal, and mechanical properties of polypropylene (PP), leading to degradation and reduced material performance. This study aims to investigate the effect of exposure length to UV on the chemical properties (functional and thermal) and mechanical properties (tensile strength) of PP. Specimens were subjected to UV exposure for 0 (control), 125, 175, 225, 275, 325, 375, and 625 days. FTIR analysis indicates UV exposure chemically degrades polypropylene (PP) by generating new oxygenated groups (–OH and C=O at 3368 cm⁻¹ and 1586 cm⁻¹) and damaging its main molecular structure (C-H at 2949 cm⁻¹, 2867 cm⁻¹, and 841 cm⁻¹). Prolonged UV exposure alters the thermal properties of polypropylene (PP), as indicated by DSC analysis, which shows broadening and shifting of the melting peak (175–180 °C) due to crystallinity changes and increased oxidation. The mechanical properties also deteriorate, with a critical reduction in tensile strength, particularly between 225 and 375 days, indicating an accelerated degradation phase. After 625 days, tensile strength declines by approximately 59%, confirming the substantial impact of extended UV exposure on PP’s durability.
Downloads
References
[1] S. Ding, C. Jin, Z. Li, D. Dun, Y. Xue, S. Leng, Y. Zhang, and H. Zhou, “Crystallization, mechanical, and heat resistance performances of copolymer polypropylene modified by α nucleating agent,” Polymer Engineering & Science, vol. 64, no. 11, pp. 5539–5550, 2024, doi: https://doi.org/10.1002/pen.26932.
[2] S. A. Stoian, A. R. Gabor, A.-M. Albu, C. A. Nicolae, V. Raditoiu, and D. M. Panaitescu, “Recycled polypropylene with improved thermal stability and melt processability,” Journal of Thermal Analysis and Calorimetry, vol. 138, no. 4, pp. 2469–2480, Nov. 2019, doi: 10.1007/s10973-019-08824-2.
[3] Balkees M. Aldabbagh, Hanaa J. Al Shimary, and Adnan R. Ahmmed, “The effect of UV – radiation on thermal and mechanical properties of (PP/LDPE) blends,” Tikrit J. Pure Sci., vol. 21, no. 1, pp. 71–75, Feb. 2023, doi: 10.25130/tjps.v21i1.952.
[4] B. Du, C. Lee, and Y. Ji, “Study of factors affecting uv-induced photo-degradation in different types of polyethylene sheets,” Polymers, vol. 16, no. 19, 2024, doi: 10.3390/polym16192709.
[5] N. M. Ainali, D. N. Bikiaris, and D. A. Lambropoulou, “Aging effects on low- and high-density polyethylene, polypropylene and polystyrene under UV irradiation: An insight into decomposition mechanism by Py-GC/MS for microplastic analysis,” Journal of Analytical and Applied Pyrolysis, vol. 158, p. 105207, 2021, doi: https://doi.org/10.1016/j.jaap.2021.105207.
[6] H. de Brouwer and N. Anbuchezhian, “The effects of UVC irradiation on the properties of thermoplastics,” Polymer Degradation and Stability, vol. 222, p. 110703, 2024, doi: https://doi.org/10.1016/j.polymdegradstab.2024.110703.
[7] W. Conradie, C. Dorfling, A. Chimphango, A. M. Booth, L. Sørensen, and G. Akdogan, “Investigating the Physicochemical Property Changes of Plastic Packaging Exposed to UV Irradiation and Different Aqueous Environments,” Microplastics, vol. 1, no. 3, pp. 456–476, 2022, doi: 10.3390/microplastics1030033.
[8] S. Kanazawa, Y. Yamada, and S. Sato, “Infrared spectroscopy of graphene nanoribbons and aromatic compounds with sp3C–H (methyl or methylene groups),” Journal of Materials Science, vol. 56, no. 21, pp. 12285–12314, Jul. 2021, doi: 10.1007/s10853-021-06001-1.
[9] N. Kozlov and R. Fairushin, “Using Fourier spectroscopy for the assessment of oxidative degradation of polypropylene medical meshes,” JBPE, vol. 3, no. 2, p. 020310, 2017, doi: 10.18287/JBPE17.03.020310.
[10] E. Andreassen, “Infrared and Raman spectroscopy of polypropylene,” in Polypropylene: An A-Z reference, J. Karger-Kocsis, Ed., Dordrecht: Springer Netherlands, 1999, pp. 320–328. doi: 10.1007/978-94-011-4421-6_46.
[11] E. A. Sagitova, P. Donfack, G. Yu Nikolaeva, K. A. Prokhorov, P. P. Pashinin, P. M. Nedorezova, A. N. Klyamkina, and A. Materny, “New insights into the structure of polypropylene polymorphs and propylene copolymers probed by low-frequency Raman spectroscopy,” Journal of Physics: Conference Series, vol. 826, no. 1, p. 012006, Mar. 2017, doi: 10.1088/1742-6596/826/1/012006.
[12] S. Subhash and E. A. Cudney, “Gamified learning in higher education: A systematic review of the literature,” Computers in Human Behavior, vol. 87, pp. 192–206, Oct. 2018, doi: 10.1016/j.chb.2018.05.028.
[13] A. Kržan, “Highly oxidized polymers as an extreme of (bio)degradable polymers,” Journal of Molecular Structure: THEOCHEM, vol. 902, no. 1, pp. 49–53, 2009, doi: https://doi.org/10.1016/j.theochem.2009.02.008.
[14] B. C. Smith, “The infrared spectra of polymers, VII: Polymers with carbonyl (C=O) bonds,” Spectroscopy, vol. 37, no. 8, pp. 10–13, 2022, doi: 10.56530/spectroscopy.tz9280y5.
[15] P. He, Y. Xiao, P. Zhang, N. Zhu, X. Zhu, and D. Yan, “In situ fourier transform infrared spectroscopic study of the thermal degradation of isotactic poly(propylene),” Applied Spectroscopy, vol. 59, no. 1, pp. 33–38, 2005, doi: 10.1366/0003702052940576.
[16] S. Qian, T. Igarashi, and K. Nitta, “Thermal degradation behavior of polypropylene in the melt state: molecular weight distribution changes and chain scission mechanism,” Polymer Bulletin, vol. 67, no. 8, pp. 1661–1670, Nov. 2011, doi: 10.1007/s00289-011-0560-6.
[17] P. Gijsman, G. Meijers, and G. Vitarelli, “Comparison of the UV-degradation chemistry of polypropylene, polyethylene, polyamide 6 and polybutylene terephthalate,” Polymer Degradation and Stability, vol. 65, no. 3, pp. 433–441, 1999, doi: https://doi.org/10.1016/S0141-3910(99)00033-6.
[18] H. Zhu, H. Yang, Y. Zhao, and D. Wang, “The dynamic crystallization and multiple melting behavior of polypropylene in the in‐reactor alloy: A differential scanning calorimetry study,” J of Applied Polymer Sci, vol. 121, no. 3, pp. 1372–1383, Aug. 2011, doi: 10.1002/app.33469.
[19] Y. Lukanina, A. Khvatov, N. Kolesnikova, and P. Anatoliy, “The effect of cooling rate during crystallization on the melting behavior of polypropylenes of different chemical structure,” ChChT, vol. 10, no. 4, pp. 479–483, Sep. 2016, doi: 10.23939/chcht10.04.479.
[20] J. Nisar, M. A. Khan, M. Iqbal, A. Shah, R. A. Khan, M. Sayed, and T. Mahmood, “Comparative Study of Kinetics of the Thermal Decomposition of Polypropylene Using Different Methods,” Adv Polym Technol, vol. 37, no. 4, pp. 1168–1175, Jun. 2018, doi: 10.1002/adv.21776.
[21] K. Pielichowski, J. Njuguna, and T. M. Majka, “Mechanisms of thermal degradation of polymers,” in Thermal Degradation of Polymeric Materials (Second Edition), Second Edition., K. Pielichowski, J. Njuguna, and T. M. Majka, Eds., Elsevier, 2023, pp. 9–11. doi: https://doi.org/10.1016/B978-0-12-823023-7.00001-0.
[22] K. G. de Castro Monsores, A. O. da Silva, S. de Sant’ana Oliveira, S. N. Monteiro, and R. P. Weber, “Evaluation of low-density polyethylene thermomechanical and fractographic behavior after ultraviolet radiation exposure,” in 23rd Brazilian Conference on Materials Science and Engineering, in Materials Science Forum, vol. 1012. Trans Tech Publications Ltd, Nov. 2020, pp. 73–78. doi: 10.4028/www.scientific.net/MSF.1012.73.
[23] N. M. Ainali, D. N. Bikiaris, and D. A. Lambropoulou, “Physicochemical alterations on UV aged polymers leading to microplastics formation: A multi-tiered study of polyester, polycarbonate and polyamide,” Polymer Degradation and Stability, vol. 222, p. 110692, 2024, doi: https://doi.org/10.1016/j.polymdegradstab.2024.110692.
[24] K. Murata, Y. Sakata, and M. Brebu, “Thermal degradation of polyethylene in the presence of a non-acidic porous solid by a continuous flow reactor,” Journal of Analytical and Applied Pyrolysis, vol. 161, p. 105395, 2022, doi: https://doi.org/10.1016/j.jaap.2021.105395.
[25] K. Pielichowski, J. Njuguna, and T. M. Majka, “Thermal degradation of high temperature-resistant polymers,” in Thermal Degradation of Polymeric Materials (Second Edition), Second Edition., K. Pielichowski, J. Njuguna, and T. M. Majka, Eds., Elsevier, 2023, pp. 187–211. doi: https://doi.org/10.1016/B978-0-12-823023-7.00003-4.
[26] H. Wu, Y. Zhao, X. Dong, L. Su, K. Wang, and D. Wang, “Probing into the microstructural evolution of isotactic polypropylene during photo-oxidation degradation,” Polymer Degradation and Stability, vol. 183, p. 109434, 2021, doi: https://doi.org/10.1016/j.polymdegradstab.2020.109434.
[27] R. Naveen, M. Kumar, M. Ramesh, R. Abinaya, and M. S. Prasath, “An investigation on effect of ultraviolet (UV) rays on mechanical properties of epoxy laminates,” Materials Today: Proceedings, 2023, doi: https://doi.org/10.1016/j.matpr.2023.06.257.
[28] S. Kazemipour, O. J. O. III, M. Porfiri, and P. Zhang, “Photochromic webbing structures for monitoring UV-induced mechanical strength degradation,” Smart Materials and Structures, vol. 33, no. 10, p. 105001, Sep. 2024, doi: 10.1088/1361-665X/ad717a.
[29] J. R. Isidoro, L. A. Souza, D. A. Simon, C. L. Petzhold, and D. Gamba, “Polystyrene containing 2-[3-(2H-benzotriazol-2-yl)-4-hydroxyphenyl]ethyl methacrylate with Low Molecular Weight Used As Macroadditive Photostabilizer,” Polymer Degradation and Stability, vol. 225, p. 110776, 2024, doi: https://doi.org/10.1016/j.polymdegradstab.2024.110776.
[30] N. M. Ainali, D. Kalaronis, E. Evgenidou, G. Z. Kyzas, D. C. Bobori, M. Kaloyianni, X. Yang, D. N. Bikiaris, and D. A. Lambropoulou, “Do poly(lactic acid) microplastics instigate a threat? A perception for their dynamic towards environmental pollution and toxicity,” Science of The Total Environment, vol. 832, p. 155014, 2022, doi: https://doi.org/10.1016/j.scitotenv.2022.155014.
[31] S. Sumari, N. Nazriati, F. Fajaroh, A. Santosa, and L. Rizqiyah, “Efek radiasi sinar matahari dan sinar ultra violet pada plastik styrofoam kemasan makanan dan minuman,” Journal Cis-Trans, vol. 3, no. 1, pp. 23–33, Nov. 2019, doi: 10.17977/um0260v3i12019p023.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2025 Andri Saputra, Tria Madeline Sitinjak, Warmiati, Indri Hermiyati, Wahyu Ratnaningsih, Asful Hariyadi, Dennis Farina Nurry
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.