PENGARUH PENAMBAHAN SERAT KAYU PINUS DAN BAMBU PETUNG TERHADAP KUALITAS PAPAN SERAT KERAPATAN SEDANG KAYU MAHANG DENGAN PEREKAT ASAM MALAT
Main Article Content
Abstract
Properties and quality of fibreboard products are much influenced by quality of the fiber materials, pressing process,
and the amount and type of the used adhesive. The use of malic acid adhesives in the manufacture of medium density
f
ibreboards (MDF) from mahang wood has low mechanical properties, especially modulus of static value. This paper
studies on the effect of adding long fibers of pine wood and petung bamboo to improve the properties of MDF mahang
wood with malic acid adhesives. The compositions ratio of mahang wood, pine wood, and petung bamboo fiber are
100/0/0, 90/10/0, 80/20/0, 90/0/10, 80/0/20, and 80/10/0, malic acid content of 25 wt % based on dry
weight fibers and hot pressing at 180ºC for 10 minutes. Physical and mechanical tests were accomplished according to
JIS 5905-2003 testing standard. Result shows the addition of long fibers of pine wood and petung bamboo increased
the mechanical value of MDF from mahang wood. The best mixture of fiber is 90% mahang wood fiber and 10%
petung bamboo, with value internal bonding 0.7 MPa, modulus of rupture 9.11 Mpa, and modulus of elasticity 2.5
GPa.
Article Details
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
References
Aisyah, H.A., Paridah, M.T., Sahri, M.h., Anwar, U.M.K., and Astimar, A.A., 2013. Properties of medium density fibreboard (MDF) from kenaf (Hibiscus cannabinus L.) core as function of refining conditions. Composites; part B. 44 : 592-596
Benthein, J.T., Heldner, S., and Ohlmeyer, M., 2017. Investigation of the interrelations between defibration conditions, fiber size and medium density fiberboard (MDF) properties. Eur. J. Wood Prod 75:215-232
Benthien, J.T., Bahnisch, C., Heldner, S., and Ohlmeyer, M. 2014. Effect of fiber size distribution on medium density fiberboard properties caused by varied steam time and temperature of defibration process. Wood Fiber Sci. 46(2): 175-185
Groom, L., Mott, L., and Shaler, S., 1999. Realationship between fiber furnish properties and structural performance of MDF. 33rd. International particleboard/composite material symposium 1999. 13-15 April 1999. Pullman, Washington. USA.
Hiziroglu, S., and Suzuki, S.V., 2007. Evaluation of surface roughness of commercially manufactured particleboard and medium density fiberboard in Japan. Journal of Meterial Process Technology 184 (1-3): 436-440.
International Agency for Research on cancer (IARC). 2012. Chemical agents and related occupations. Volume 100 F: A Review of Human Carcinogens, WHO. France
Japanese Standard Association. 2003. Japanese Industrial Standard for Fiberboards A 5905. Japanese Standard Association. Tokyo
Kusumah, S.S., Umemura, K., Yoshioka, K., Miyafuji, H., and Kanayama, K., 2016. Utilization of sweet sorghum bagasse and citric acid for manufacturing of particleboard I : Effects of pre-drying treatment and citric acid content on the board properties. Industrial Crops and Products 84 ; 34-42.
Kusumah, S.S., Umemura, K., Yoshioka, K., Miyafuji, H., and Kanayama, K., 2017. Utilization of sweet sorghum bagasse and citric acid for manufacturing of particleboard II : influences of pressing temperature and time on particleboard properties. Journal of Wood Science 63(2):161-172
Myers, G.C., 1983. Relationship of fiber preparation and characteristics to performance of medium density hardboards. For Prod. J 33(10): 43-51
Nemli, G., Ozturk, I., and Ayudin, A., 2005. Some of parameters influencing surface roughness of particleboard. Building and Enviroment 40: 1337-1340
Roffael, E. 1993. Formaldehyde release from particle board and other wood based panels. Kuala Lumpur: FRIM Kepong
Shi, J.I., Zhang, S.Y., and Riedl, B., 2006. Multivariate modeling of MDF panel properties in relation to wood fiber characteristics. Holzforsschung 60:285-293
Sugawara, R and K. Umemura. 2014. Bonding composition and board. United States Patent. No. US 2014/0011042 A1.
Syamani, F.A, and Munawar, S.S., 2013. Eco friendly board from oil palm frond and citric acid. Wood Research Journal. Vol. 4 No. 2 : 72-75
Umemura, K., O. Sugihara, and S. Kawai. 2013. Investigation of a new natural adhesive composed of citric acid and sucrose for particleboard. J Wood Sci. (59), 203-209.
Umemura, K., T. Ueda, SS. Munawar and S. Kawai. 2012. Application of citric acid as natural adhesive for wood. Journal of Applied Polymer Science (123), 1991-1996.
Vukusic SB., D. Katovic, C. Schramm, J. Trajkovic and B. Sefc. 2006. Polycarboxylic acids as non formaldehyde anti swelling agents for wood. Holzforschung(60), 439-444.
Wahyudi, A., Prayitno, T.A., Widyorini, R., and Sutapa, J.P.G., 2018. Pengaruh jumlah perekat asam malat terhadap sifat papan serat kerapatan sedang kayu mahang. Dalam Nanang Masruchin (Eds). Prosiding ilmiah Nasional Seminar Ligoselulosa 2018. Hal : 127-132.
Widyorini, R., Dewi, G.K., Nugroho, W.D., Prayitno, T.A., Jati, A.S., and Tejolaksono, M.N., 2018. Properties of citric acid bonded composite board from elephant dung fibers. J. Korean Wood sci. technol. 46(2): 132-142
Widyorini, R., Umemura, K., Isnan, R., Putra, D.R., Awaludin, A., and Prayitno, T.A., 2016. Manufacture and properties of citric caids bonded particleboard made from bamboo materials. European Journal of wood and Wood Product 71 (1) : 57-65.
Xing, C., J. Deng, and SY. Zhang. 2007. Effect of thermo mechanical refining on properties of MDF made from black spruce bark. Wood Sci Technol (41). 329-338.