Tingkat Redam Suara Dan Ketahanan Papan Partikel Campuran Serbuk Kayu Sengon Dan Mesocarp Kelapa Sawit Terhadap Serangan Rayap Tanah KUALITAS REDAM SUARA PAPAN PARTIKEL MESOCARP KELAPA SAWIT
Article Sidebar
Main Article Content
Abstract
The increase in palm oil production in Indonesia produces significant volumes of waste, including empty fruit bunches (EFB), shells, and fibers. This waste has the potential to be processed into particleboard, with the addition of sawdust to improve physical properties and termite resistance. An additional raw material is Sengon wood (Falcataria moluccana (Miq.)), which was chosen due to its economic value and fast-growing nature. The purpose of this study was to determine its physical properties, resistance to subterranean termite attacks, and sound attenuation level. Particleboard was made from a mixture of oil palm mesocarp fiber and Sengon wood particles using urea formaldehyde (UF) adhesive with a concentration of 18%. The raw material combinations of oil palm mesocarp fiber and Sengon wood particles were 0:100, 25:75, 50:50, 75:25, and 100:0. Hot pressing was carried out at a pressure of 25 kg/cm² and a temperature of 130 °C for 10 minutes. The results of the study showed that the physical properties of the material ranged from 0.37 to 0.39 g/cm, water content from 7.27% to 9.45%, thickness expansion from 5.94% to 11.71%, and water absorption from 96.53% to 149.79%. The resistance of the board to subterranean termite attacks, achieved with a combination of oil palm mesocarp and sengon powder 75:25%, resulted in the highest termite mortality. In comparison, the combination of oil palm mesocarp and sengon wood powder (100:0%) experienced the highest weight loss. The best sound attenuation level was achieved with a combination of oil palm mesocarp and sengon wood powder 0:100%.
Article Details
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
References
Anggraini, R., Khabibi, J., & Adelka, Y.F. (2021). Karakteristik papan partikel dari campuran limbah akasia (Acacia mangium Willd.) dan kulit kelapa muda (Cocos nucifera L.). Jurnal Silva Tropika, 5(1), 366-381.
Abdurachman & Hadjib, N. (2020). Sifat papan partikel dari kayu kulit manis (Cinnamomum burmanii BL). Jurnal Penelitian Hasil Hutan, 9(2):128-141. Anistasya, N.F., Hendri, D., & Fauziah, I.Y. (2024). Penggunaan serbuk gergaji kayu sengon sebagai soundproofing pada dinding dan lantai kos putri rahayu Studi Kasus: (Kamar Tidur Kos Putri Rahayu). Prosiding Seminar Karya & Pameran Arsitektur Indonesia (hal. 410-428).
Arinana, Philippines, I., Bahtiar, E.T., Koesmaryono, Y., Nandika, D., Rauf, A., ... & Sumertajaya, I.M. (2016). Coptotermes curvignathus Holmgren (Isoptera: Rhinotermitidae) capability to maintain the temperature fluctuation inside its nests. Journal of Entomology, 13(5-6), 199-202.
Astari, L., Syamani, F. A., & Prasetiyo, K.W. (2019). Sifat fisik, mekanik dan akustik papan partikel berbahan dasar batang jagung (Zea mays L). Jurnal Riset Industri Hasil Hutan, 11(1), 41-52.
American Society for Testing and Materials (ASTM). (2010). Classification for Rating Sound Insulation (ASTM-E413-10). ASTM International.
Alim, M. I., & Anggoro, D. (2017). Pengukuran Transmission Loss (TL) dan Sound Transmission Class (STC) pada Suatu Sampel Uji. Diakes dari DOI: 10.13140/RG.2.2.19507.17448
Athariqa, D., Selvi, M. O., & Dicky, D. (2022).Urea-Formaldehid Konsentrat Sebagai Bahan Baku Resin Urea-Formaldehid. Jurnal Teknologi Ramah Lingkungan, 6(1), 11-21.
Rifaida, E., Mukti, W., & Rini, M. 2014. Pembuatan dan karakterisasi peredam suara dari bahan baku serat alam. Jurnal Arena Tekstil 29(1), 1-8.
Fransiskus, H., Hartono, R., & Sucipto, T. (2015). Kualitas Papan Partikel dari Campuran Sabut Kelapa dan Partikel Mahoni dengan Berbagai Variasi Kadar Perekat Phenol Formaldehida. Peronema Forestry Science Journal, 4(2), 53-61.
Haryanti, A., Norsamsi, N., Sholiha, P. S. F., & Putri, N. P. (2014). Studi pemanfaatan limbah padat kelapa sawit. Konversi, 3(2), 20-29.
Haygreeen, J.G., & Bowyer, J.L. (1996). Hasil hutan dan ilmu kayu. Suatu pengantar. Hadikusuma S.A., Penerjemah: Prawiro, H.S., editor. Terjemahan dari: Forest Product and Wood Science, An Introduction. Gajah Mada University Press. Yogyakarta.
Indrayani, Y., & Fatmawati, D. (2019). Effect of bait density on consumption rates and mortality of subterranean termite Coptotermes curvignathus. Journal of Biological Researches, 24(2), 90-94.
Kuswarini, S. (2009). Papan partikel dari tandan kosong kelapa sawit. Jurnal Riset Industri, 3(3). 185-189.
Laksono, A.D., Ernawati, L., & Maryanti, D. (2019). Pengaruh fraksi volume komposit polyester berpenguat limbah serbuk kayu bangkirai terhadap sifat material akustik. Jurnal Rekayasa Mesin, 10(3), 277-285.
Lestari, R.Y., Harsono, D., Cahyana, B.T., Atmaja, B.T., & Asmoro, W.A. (2018). Tingkat redaman suara papan komposit dari tandan kosong kelapa sawit dan serbuk kayu akasia. Prosiding Seminar Nasional Teknologi dan Inovasi Industri Tahun (hal. 31-38).
Maloney, T.M. (1993). Modern Particleboard and Dry Process Fiberboard Manufactoring. Miller Freeman Inc, New York.
Maulida, N.A. (2021). Pengaruh jenis perekat pada uji keawetan papan partikel dari Serat tandan kosong kelapa Sawit dan serbuk batang tembakau terhadap serangan rayap tanah (Skripsi Sarjana). Universitas Brawijaya, Malang.
Mikael, I., Hartono, R., & Sucipto, T. (2015). Kualitas papan partikel dari campuran ampas tebu dan partikel mahoni dengan berbagai variasi kadar perekat phenol formaldehida. Peronema Forestry Science Journal, 4(2), 45-52.
Nugroho, T. A., & Salamah, Z. (2015). Pengaruh lama perendaman dan konsentrasi biji sengon (Paraserianthes falcataria L.). JUPEMASI-PBIO, 9(8), 230-236.
Nugroho. (2008). Rancangan Percobaan. UNIB Press.
Purwanto, D., Riset, B., & Banjabaru, S. I. (2016). Sifat fisis dan mekanis papan partikel dari limbah campuran serutan rotan dan sebuk kayu. Jurnal Riset Industri, 10(3), 125-133.
Putra, A. S. (2020). Penentuan koefisien serap bunyi papan partikel dari limbah pelepah kelapa Sawit. Jurnal Surya Teknika, 7(2), 182-185.
Raymond, D., Berendt & Edith, L. R. Corliss (1976). Quieting: A Practical Guide
to Noise Contol. National Bureau of Standards Handbook 119. U.S. Government Printing Office, Washington.
Rislyana, F., Harlia, Sitorus B. (2015). Bioaktivitas ekstrak batang kecombrang (Etlingera elatior (Jack) R.M.Sm.) terhadap rayap Coptotermes curvignathus sp. Jurnal Kimia Khatulistiwa 4(3): 9- 15.
Roza, D., Dirhamsyah, M, Nurhaida. (2015). Sifat fisik dan mekanik papan partikeldari kayu sengon (Paraserianthes falcataria. L) dan serbuk sabut kelapa (Cocos nucifera. L). Jurnal Hutan Lestari, 3(3), 374-382.
Sadik, R., & Amalia, R. (2023). Produksi dan karakterisasi material komposit peredam suara berbahan serat alam dengan metode ssintetik Hand Lay-Up. Jurnal Ilmiah Bidang Ilmu Kerekayasaan, 44(2), 130-138.
Suandi, A. (2009). Karakteristik ssound transmission loss pintu akustik yang digunakan sebagai penghalang kebisingan. Jurnal Purifikasi, 10(2), 125–132.
Standar Nasional Indonesia (SNI). (2006). Papan Partikel (SNI 03-2105-2006). Badan Standarisasi Nasional.
Sornnuwat Y. (1996). Wood Consumption and survival of ssubterranean termite Coptotermes gestroi Wasmann. Proceedings The 1996 Annual Meeting of International Research Group on Wood Preservation. Stockholm. Sweden.
Susilo, Y.D. (2017). Kandungan selulosa, hemiselulosa dan lignin serat sawit hasil fermentasi jamur pelapuk. (Skripsi Sarjana). Universitas Hasanudin, Makassar.
Siahaan, M. Y. R., & Darianto, D. (2020). Karakteristik koefisien sserap suara material concrete foam dicampur sserat Tandan Kosong Kelapa Sawit (TKKS) dengan metode Impedance Tube. Journal of Mechanical Engineering Manufactures Materials and Energy, 4(1), 85-93.
Tampubolon, A.E., Oemry, S., & Lubis, L. (2015). Uji daya hidup rayap tanah (Coptotermes curvignathus Holmgren) (Isoptera: Rhinotermitidae) dalam berbagai media kayu di laboratorium. Jurnal Online AgroekoteaknologiI, 3(3), 864-869.
Trisanti, P. N., HP, S. S., Nura’ini, E., & Sumarno, S. (2018). Ekstraksi selulosa dari serbuk gergaji kayu sengon melalui proses delignifikasi alkali ultrasonik. Jurnal Sains Materi Indonesia, 19(3), 113-119.
Viviana, M., & Tavita, G. E. (2019). Keawetan papan partikel dari batang sorgum dan kayu akasia dengan perekat Urea Formaldehida terhadap serangan rayap tanah. Jurnal Hutan Lestari, 7(2), 763-772.
Zhang, J., Song, F., Tao, J., Zhang, Z., & Shi, S. Q. (2018). Research progress on formaldehyde emission of wood-based panel. International Journal of Polymer Science 2018. doi:10.1155/2018/9349721.