PENENTUAN DAN APLIKASI FORMULA PEREKAT NABATI DARI EKSTRAK KULIT KAYU MAHONI PADA LAMINASI KAYU JABON
Main Article Content
Abstract
The domestic need for phenolic-based wood adhesives is high, but the material is currently imported, then altenative adhesives
are needed. This paper studies the characteristics of mahogany tannins and effective formulation of alternative adhesives made from
mahogany bark extracts of mixture tapioca flour and industrial flour as extender applied to composite or glued products. The bark
of mahogany was cut to the size of 2 cm x 1 cm x 0.1 cm, extracted with hot water (70–80°C) with a ratio of 1:3 (w/w,
material/water) for 3 hours with two repetitions. After extraction product was filtered, and the filtrate was copolymerized using
resorcinol and formaldehyde under alkaline and room temperature conditions to produce resin tannin resorcinol formaldehyde
(TRF). The blend of tapioca flour and industrial flour (1:1, w/w) as an extender was used in the TRF application to manufacture
composite products. The results showed that this mahogany bark liquid extract could be copolymerized to form a resin which then
applied as a wood adhesive in a cold pressing process. The optimum adhesive formula was a mixture of 0.25 mol of resorcinol and
1-mol formaldehyde, with a 15% extender, and a catalyst (NaOH 40%) of 4% of the total weight of the adhesive formulation.
The characteristics of mahogany tannin adhesives resemble those of the exterior type phenolic group.
Article Details
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
References
Akzonobel. (2001). Synteko phenol-resorcinol adhesive 1711 with hardeners 2620, 2622, 2623. Casco Adhesive, Asia.
Falah, S., Suzuki, T., & Katayama, T. (2008). Chemical constituents from Swietenia macrophylla bark and their antioxidant activity. Pakistan Journal of Biological Sciences, 11(16), 2007–2012. doi: 10.3923/pjbs.2008.2007.2012.
Japanese Agricultural Standard (JAS). (2003). Glued laminated timber (JAS 234-2003). Japanese Plywood Inspection Corporation (JPIC).
Kemenperin, (Kementerian Perindustrian RI). (2019, March 17). Agresif dobrak pasar ekspor, industri furnitur dan kerajinan raih surplus. Siaran Pers. doi://www.kemenperin.go.id/ artikel/20443/Agresif-Dobrak-Pasar-Ekspor,-Industri-Furnitur-dan-Kerajinan-Raih-Surplus pada tanggal 16 Maret 2021
Lestari, A. S. R. D., Hadi, Y. S., Hermawan, D., & Santoso, A. (2015). Glulam properties of fast-growing species using mahogany tannin adhesive. BioResources, 10(4), 7419–7433. doi: 10.15376/biores.10.4.7419-7433.
Lestari, A. S. R. D., Hadi, Y. S., Hermawan, D., Santoso, A., & Pizzi, A. (2019). Physical and mechanical properties of glued–laminated lumber from fast-growing tree species using mahogany tannin adhesive. Wood and Fiber Science, 51(2), 1–12. doi: 10.22382/ wfs-2019-xxx.
Pari, R., Abdurachman, & Santoso, A. (2019). Keteguhan rekat dan emisi formaldehida papan lamina rotan menggunakan perekat tanin formaldehida. Jurnal Penelitian Hasil Hutan, 37(1), 33–41. doi: 10.20886/JPHH.2019.37 .1.33-41.
Qodri, U. L., Masruri, & Utomo, E. P. (2014). Skrining fitokimia metabolit sekunder ekstrak metanol dari kulit batang mahoni (Swietenia mahagony Jacq.). Jurnal Ilmu Kimia Universitas Brawijaya, 2(2), 480–484. doi://kimia.student journal.ub.ac.id/index.php/jikub/article/view/ 529/210.
Rosdiana, N. A., Dumarçay, S., Gérardin, C., Chapuis, H., Santiago-Medina, F. J., Sari, R. K., Syafii, W., Gelhaye, E., Raharivelomanana, P., Mohammed, R., & Gérardin, P. (2017). Characterization of bark extractives of different industrial Indonesian wood species for potential valorization. Industrial Crops and Products, 108, 121–127. doi: 10.1016/j.indcrop. 2017.06.034.
Santoso, A. (2003). Sintesis dan karakterisasi resin lignin resorsinol formaldehida untuk perekat kayu lamina. Desertasi Doktor. Institut Pertanian Bogor, Bogor.
Santoso, A., & Abdurachman. (2016). Karakteristik ekstrak kulit kayu mahoni sebagai bahan perekat kayu. Jurnal Penelitian Hasil Hutan, 34(4), 269–284. doi: 10.20886/jphh.2016.34.4. 269-284.
Santoso, A., Hadi, Y. S., & Malik, J. (2014). Composite flooring quality of combined wood species using adhesive from merbau wood extract. Forest Products Journal, 64(5–6), 179–186. doi: 10.13073/FPJ-D-13-00051.
Standar Nasional Indonesia (SNI). (2000). Fenol formaldehida cair untuk perekat kayu lapis (SNI 4567-2000). Badan Standardisasi Nasional, Jakarta.
Sobur, A. (2021, January 30). Target ekspor tak tercapai, industri mebel dan kerajinan dapat secercah pintu rezeki di akhir tahun 2020. Himpunan Industri Mebel Dan Kerajinan Indonesia (HIMKI). Diakses dari https://www. himki-indonesia.com/post/ view/253-id-target -ekspor-tak-tercapai-industri-mebel- dan- kerajinan-dapat-secercah-pintu-rezeki-di-akhir-tahun -2 pada tanggal 30 Maret 2021.
Steel, R. G. D., & Torrie, J. H. (1990). Principles and procedure of statistic. New York: Mc. Graw Hill Book Company.
Tahir, P. M., Halip, J. A., & Lee, S. H. (2019). Tannin-based bioresin as adhesives. Dalam Lignocellulose for Future Bioeconomy (pp. 109–133). Elsevier. doi: 10.1016/B978-0-12-816354-2.00007-4.
Triwahyuono, D. A., & Hidajati, N. (2020). Uji fitokimia ekstrak etanol kulit batang mahoni (Swietenia mahagoni Jacq.). UNESA Journal of Chemistry, 9(1), 54–57. doi://jurnalmahasiswa. unesa.ac.id/ index. php/ unesa- journal- of- chemistry/article/view/32784.
Tsoumis, G. T. (1991). Science and technology of wood : structure, properties, utilization. Dalam Science and technology of wood. Structure, properties, utilization. Van Nostrand Reinhold.
Wisnubroto, K. (2020, November 17). Industri mebel bising kembali. Portal Informasi Indonesia. doi://indonesia.go.id/narasi/indonesia-dalam-angka/ekonomi/industri-mebel-bising-kembali.